Magnesium hydroxide

Magnesium hydroxide (Mg(OH)2)Provide surface treatment according to clients. Accord with EU RoSH.

1. Brief Introduction

In order to produce fire retardant magnesium hydroxide, it must be fine crystal shape, small average particle size, small specific surface area, prone to decentralize, hard to reunite and surface polarity eliminated. Adopt synthesized techniques on magnesium chloride as raw material, treat magnesium hydroxide with hot water, and then make it a fire retardant which can be used in plastic and rubber through surface treatment to have the characteristic of low initial decompose temperature and 10% more heat absorptivity compared with aluminium hydroxide. It can be applied in PE, PVC, PP, and also in PET, PBT, PA, PPO, and ABS and so on.

Our tenet is to develop fire retardant magnesium hydroxide of wide range of application.

2. Performance index

index                Model	FR-H		FR-S
	MH-01	MH-02
Mg(OH)2 ≥%	99	96	95
Brightness ≥	95	90	92
Acid insoluble matter ≤%	0.05	1.5	2.3
Iron (measured in Fe) ≤%	0.05	0.25	0.25
Chlorine(measured in CI) ≤%	0.3	0.4	0.4
Free water ≤%	0.5	0.3	0.3
Average particle size (um)	1.2-3	4-8	3-10
Remark: 1. Provide surface treatment according to clients. 2. Accord with EU RoHS.

3. Packing    

  20kg or 25kg polypropylene woven bag inner lining polyethylene film.

Magnesium hydroxide